Properties
Test methods
Units
Values
-
-
Productname--PA 4.6
-
Color--red brown
-
Average molar mass (average molecular weight)-106 g / mol
-
DensityISO 1183-1g / cm31,180
-
- Water apsorption
-
∙ after 24/96 h immersion in water of 23°C (1)ISO 62mg90 / 180
-
∙ after 24/96 h immersion in water of 23°C (1)ISO 62%1,3 / 2,6
-
∙ at saturation in air of 23°C / 50% RH-%2,8
-
∙ at saturation in water of 23°C-%9,5
-
- Thermal Properties (2)
-
Melting temperature (DSC, 10°C/min)ISO 11357-1/-3°C290
-
Dynamic glass transition temperature +ISO 3146°C75
-
Dynamic glass transition temperature ++ISO 3146°C
-
Thermal conductivity Lambda λ at 23°C-W / (K · m)0,300
-
- Coefficient of linear thermal expansion
-
∙ average value between 23 and 60°C-m / (m · K)80 x 10-6
-
∙ average value between 23 and 100°C-m / (m · K)90 x 10-6
-
∙ average value between 23 and 150°C-m / (m · K)
-
- Temperature of deflection under load
-
∙ method A: 1,8 MPaISO 75-1/-2°C160
-
Vicat-Erweichungstemperatur - VST/B50ISO 306°C
-
- Maximal allowable service temperature in air
-
∙ for short periods (3)-°C200
-
∙ continously: for 5.000 / 20.000 h (4)-°C150 / 130
-
Minimal service temperature (5)-°C-40
-
- Flammability (6)
-
∙ Oxygen-IndexISO 4589-1/-2%24
-
∙ according to UL 94 (3 / 6 mm thickness)--HB / HB
-
Specific heat capacity-J / (g · K)2,1
- Mechanical Properties at 23°C (7)
-
- Tension test (8)
-
∙ tensile stress at yield / tensile stress at break (9) +ISO 527-1/-2N / mm2105 / -
-
∙ tensile stress at yield / tensile stress at break (9) ++ISO 527-1/-2N / mm255 / -
-
∙ tensile strength (9) +ISO 527-1/-2N / mm2105
-
∙ tensile strain at yield (9) +ISO 527-1/-2%18
-
∙ tensile strain at break / elongation at break (9) +ISO 527-1/-2%25 / -
-
∙ tensile strain at break / elongation at break (9) ++ISO 527-1/-2%> 100 / -
-
∙ tensile modulus of elasticity (10) +ISO 527-1/-2N / mm23400
-
∙ tensile modulus of elasticity (10) ++ISO 527-1/-2N / mm21350
-
- Compression test (11)
-
∙ compressive stress at 1/2/5 % nominal strain (12) +ISO 604N / mm223 / 45 / 94
-
- Creep test in tension (8)
-
∙ stress to produce 1% strainISO 899-1N / mm222
-
stress to produce 1% strain (σ 1/1000)ISO 899-1N / mm27,50
-
Charpy impact strenght - Unnotched (12)ISO 179-1/1eUkJ / m2no break
-
Charpy impact strenght - NotchedISO 179-1/1eAkJ / m28
-
Charpy impact strength (15° V-notched, both-sided)ISO 11542-2kJ / m2
-
Izod impact strength - Notched +180/2AkJ / m28
-
Izod impact strength - Notched ++180/2AkJ / m225,00
-
Ball intentation hardness (13)2039-1N / mm2165
-
Rockwell hardness (134)ISO 2039-2N / mm2M 92
-
Shore hardness D (3 / 15 s)ISO 868N / mm2
-
Coefficient of sliding friction m (14)--0,4 - 0,6
-
Sliding wear method E (14)-µ / km
-
Sliding wear method Q (14)-µ / km18
- Electrical Properties at 23°C
-
Electric strength (15)IEC 60243-1kV / mm25
-
Electric strength (15) ++IEC 60243-1kV / mm15,00
-
Volume resistivity +IEC 60093Ω · cm> 1014
-
Volume resistivity ++IEC 60093Ω · cm> 1012
-
Surface resistivity +IEC 60093Ω> 1013
-
Surface resistivity ++IEC 60093Ω> 1012
-
- Relative permittivity ε
-
∙ at 100 Hz +IEC 60250-3,80
-
∙ at 100 Hz ++IEC 60250-7,40
-
∙ at 1 MHz +IEC 60250-3,4
-
∙ at 1 MHz ++IEC 60250-3,80
-
- Dielectric dissipation factor tan Delta δ
-
∙ at 100 Hz +IEC 60250-0,0090
-
∙ at 100 Hz ++IEC 60250-0,1300
-
∙ at 1 MHz +IEC 60250-0,019
-
∙ at 1 MHz ++IEC 60250-0,0600
-
Comparative tracking index (CTI) +IEC 60112-400
-
Comparative tracking index (CTI) ++IEC 60112-400